Our company has developed various types of inert alumina ceramic ball & covering ceramic ball products, which are broadly utilized in industries like petroleum, chemical industry, chemical fertilizer, refining chemicals, environmental protection, gas and etc., for examples, in fixed bed reaction equipments of hydrogenation, hydrogen-making and reforming isomerization. |
|
Item |
Unit |
Technical data |
Composition |
Data |
Remarks |
Bulk density |
Kg/m3 |
1250-1800 |
Al2O3 |
30-95% |
1.Al2O3&SiO2≥92%.
2.Percentage of Al2O3 & SiO2 are up to user's requirement.
3.Bulk density is just for reference, not for testing standard. |
|
Water Sorption |
% |
=1 |
SiO2 |
24-68% |
Heat conduction index |
Kcal/mhoC |
=0.7 |
Fe2O3 |
<0.5 |
Spalling resistance |
oC |
1300-1500 |
CaO |
<1.5 |
Specific heat |
Cal/goC |
0.15-0.2 |
Na2O |
<1.5 |
Refractoriness |
oC |
20-8004 (three times, without crash) |
MgO |
<1 |
Acid resistance |
% |
=99 |
K2O |
<2.5 |
Alkali resistance |
% |
=82 |
Other |
|
Hardness |
Mohs |
=6.5-7 |
|
|
|
|
Micro-pore ceramic ball |
|
Micro-pore ceramic ball (or filtration ceramic ball) has the same function of supporting & covering catalyst and diversify gas and liquid, as the function of inert alumina ceramic ball. Besides, it can adhere and filter the impurity in oil and catalyst supporting & carrier, which can protect catalyst and prolong the running period of the equipment.
|
|
Diameter of pore
(μm) |
Gas pore
(%) |
Porosity
(Pa) |
Acid resistance
(%) |
Alkali resistance
(%) |
Thermal stability
(△T)℃ |
Crushing strength
(N/pc) |
Bulk density
(kg/m3) |
1# 0.5~35 |
20~30 |
0.2~0.8m3.cm/m2.h.10 |
=99 |
=82 |
800 |
100~20000 |
1200~1500 |
2# 40~100 |
15~25 |
0.2~0.8m3.cm/m2.h.10 |
=99 |
=82 |
800 |
100~20000 |
1200~1500 |
3# 110~1000 |
15~25 |
0.2~0.8m3.cm/m2.h.10 |
=99 |
=82 |
800 |
100~20000 |
1200~1500 |
|
|
10 |
|
|
|
|
|
|
|
Alumina ceramic ball, corundum ball |
|
For the alumina (corundum) abrading ball, there are such lots of merits as, higher density, mechanical strength, well abrasive resistance etc. It is broadly applied to the areas of ceramic production, ball abrasive machine, electronics, aerospace, chemical fertilizer, and chemical industry. |
|
Physical performance |
Chemical composition |
Item |
Unit |
Technical index |
Composition |
Index |
Bulk density |
kg/m3 |
2.9-3.6 |
AL2O3 |
70-99% |
Crushing strength |
KN/pc |
10-15 |
SiO2 |
3-17% |
Hardness |
Mohs |
=7-9 |
MgO |
0.5% |
Abrasion ratio |
?/P> |
0.03 |
Fe2O3 |
0.03% |
Water sorption |
% |
<0.05 |
CaO |
0.2% |
|
|
|
Na2O |
0.1% |
|
|
|
Other |
Micro quantity |
|
|
Alumina ball |
|
Item
Aluminum (%) |
Density
(g/cm3) |
Mohs
hardness |
Crushing strength
(kgf/mm2) |
Abrasion ratio
(‰-24h) |
Water sorption
(%) |
95 |
=3.70 |
9 |
=2100 |
=0.10 |
<0.005 |
|
|
Refractory ball |
|
Refractory ball is mainly
applied as the packing in the high temperature
smelting converters. It contains higher content
of alumina, and it is capable of resisting high
temperature. |
|
Product/Index |
Percentage of Alu.
(AL2O3) |
Refractoriness
(℃) |
0.2MPa refractoriness under load porosity |
Reburning shrinkage
(1450℃,2h)% |
Porosity
(%) |
Crushing pressure under normal temperature (Mpa) |
High Alu. Refractory ball |
=23-85% |
=1700 |
=1500℃ |
+0.0,-0.4 |
=24 |
=49 |
Adhesive mud refractory ball |
=30-60% |
=1450 |
=1350℃ |
+0.0,-0.3 |
=24 |
=29.4 |
|
|
plum blossom supporting ball series |
|
Newly successfully developed plum blossom supporting ball series products are our brand-new products by using latest technology, mainly used as supporting covering packing in reaction equipments of Petroleum & chemical, hydrogenation, refining, ethane, isomerization of aromatics and etc.. They can be used in primary reformer or secondary reformer, in order to lower the pressure of inside tower. With the advantages of larger surface area, better flow volume of gas & liquid, lower burthen of inside tower, these products can attribute to obvious economic benefits. |
|
Physical performance: |
|
Product name |
Spec. |
Heaping density(kg /m3) |
|
Heat resistance
(%) |
Acid resistance
(%) |
Alkaline resistance
(%) |
Mohs hardness
(grade) |
Quenched experiment
(OC) |
Specific heat
(Cal/mh OC) |
plum blossom supporting ball |
F6 |
1100-1400 |
|
1300-1500 |
99 |
82 |
7 |
20-800 |
0.15-0.2 |
plum blossom supporting ball |
F8 |
1180-1400 |
|
1300-1500 |
99 |
82 |
7 |
20-800 |
0.15-0.2 |
plum blossom supporting ball |
F10 |
1150-1350 |
|
1300-1500 |
99 |
82 |
7 |
20-800 |
0.15-0.2 |
plum blossom supporting ball |
F13 |
1140-1350 |
|
1300-1500 |
99 |
82 |
7 |
20-800 |
0.15-0.2 |
plum blossom supporting ball |
F15 |
1130-1320 |
|
1300-1500 |
99 |
82 |
7 |
20-800 |
0.15-0.2 |
plum blossom supporting ball |
F19 |
1120-1300 |
|
1300-1500 |
99 |
82 |
7 |
20-800 |
0.15-0.2 |
plum blossom supporting ball |
F25 |
1100-1300 |
|
1300-1500 |
99 |
82 |
7 |
20-800 |
0.15-0.2 |
plum blossom supporting ball |
F30 |
1100-1290 |
=1 |
1300-1500 |
99 |
82 |
7 |
20-800 |
0.15-0.2 |
plum blossom supporting ball |
F40 |
1100-1280 |
=1 |
1300-1500 |
99 |
82 |
7 |
20-800 |
0.15-0.2 |
plum blossom supporting ball |
F50 |
1100-1270 |
=1 |
1300-1500 |
99 |
82 |
7 |
20-800 |
0.15-0.2 |
plum blossom supporting ball |
F60 |
1100-1260 |
=1 |
1300-1500 |
99 |
82 |
7 |
20-800 |
0.15-0.2 |
|
|
Chemical composition: |
|
AL2O3 ( %) |
SiO2 ( %) |
Fe2O3 ( %) |
CaO ( %) |
Na2O ( %) |
MgO ( %) |
K2O ( %) |
other |
23-90 |
68-2 |
<0.5 |
<1.8 |
<0.5 |
<0.15 |
<1.5 |
burned |
|
|
|